EAA 1430真貨原廠產(chǎn)地 盛禧奧(斯泰隆) EAA1430物性表

物理性能測試條件測試方法測試結(jié)果單位密度 / 比重
g/cm3ASTM D-7920.93
g/cm3ISO 11830.93
ASTMD792,ISO11830.930g/cm3熔體質(zhì)量流動速率2190°C/2.16kgASTMD1238,ISO11335.0g/10min共聚單體含量3
內(nèi)部方法9.7%機械性能測試條件測試方法測試結(jié)果單位抗張強度屈服,模壓成型4ASTMD6387.67Mpa屈服,模壓成型ISO527-2/5087.67Mpa斷裂,模壓成型4ASTMD63819.5Mpa斷裂,模壓成型ISO527-2/50819.5Mpa伸長率斷裂,模壓成型4ASTMD638580%斷裂,模壓成型ISO527-2/508580%拉伸屈服強度Compression MoldedMPaASTM D-6387.67Compression MoldedMPaISO 527-2/5087.67拉伸斷裂強度Compression MoldedMPaASTM D-63819.5Compression MoldedMPaISO 527-2/50819.5拉伸斷裂伸長率Compression Molded%ASTM D-638580Compression Molded%ISO 527-2/508580薄膜厚度-Tested
um
50.8拉伸屈服強度(MD)50.8umMPaASTM D-88210.4拉伸屈服強度(TD)50.8umMPaASTM D-88210.2拉伸屈服強度(MD)50.8umMPaISO 527-310.4拉伸屈服強度(TD)50.8umMPaISO 527-310.2拉伸斷裂強度(TD)50.8umMPaASTM D-88231.0拉伸斷裂強度(MD)50.8umMPaASTM D-88230.6拉伸斷裂強度(TD)50.8umMPaISO 527-331拉伸斷裂強度(MD)50.8umMPaISO 527-330.6拉伸斷裂伸長率(MD)50.8um%ASTM D-882420拉伸斷裂伸長率(TD)50.8um%ASTM D-88247050.8um%ISO 527-3470拉伸斷裂伸長率(MD)50.8um%ISO 527-3420埃爾曼多夫撕裂強度(MD)50.8umgASTM D-1922470埃爾曼多夫撕裂強度(TD)50.8umgASTM D-1922730埃爾曼多夫撕裂強度(MD)50.8umNISO 埃爾曼多夫撕裂強度(TD)50.8umNISO 光學(xué)性能測試條件測試方法測試結(jié)果單位光澤度45°，50.8um
ASTM D-245774霧度（Haze）50.8um%ISO um%ASTM D-10034熔體溫度
℃
196光澤度45°,50.8μmASTMD245774
霧度（Haze）50.8μmASTMD10034.0%50.8μmISO147824.0%熱性能測試條件測試方法測試結(jié)果單位維卡軟化溫度
ASTMD1525,ISO30676.1°C溶融溫度（DSC）
內(nèi)部方法96.1°C維卡軟化點
℃ASTM D-152576.1
℃ISO 30676.1熔融溫度
℃Internal Method96.1薄膜測試條件測試方法測試結(jié)果單位埃爾曼多夫抗撕強度5MD:51μmASTMD1922470gTD:51μmASTMD1922730gMD:51μmISONTD:51μmISON抗張強度MD:屈服,51μmASTMD88210.4MpaTD:屈服,51μmASTMD88210.2MpaMD:屈服,51μmISO527-310.4MpaTD:屈服,51μmISO527-310.2MpaMD:斷裂,51μmASTMD882,ISO527-330.6MpaTD:斷裂,51μmASTMD882,ISO527-331.0Mpa伸長率MD:斷裂,51μmASTMD882,ISO527-3420%TD:斷裂,51μmASTMD882,ISO527-3470%基本性能測試條件測試方法測試結(jié)果單位熔體流動速率190℃/2.16kgg/10minASTM D-12385190℃/2.16kgg/10minISO 11335單體含量
%Internal Method9.7